ASTM D1414
TensileTesting of rubber O-rings (tensile strength, elongation using spool fixtures).
Rubber, elastomers & foams
Rubber Testing Machine
Filter by test type, industry or standards body, or search a designation directly. Where a method has an equivalent under another body, both are shown.
ASTM D1871
Peel & adhesionAdhesion of single-strand bead wire to rubber (tyre bead construction).
ASTM D2632-adjacent note
TensileResilience, flexometer and DeMattia flex tests require dedicated instruments and are companions to UTM testing.
ASTM D3574
TensileFlexible cellular materials — slab, bonded and molded urethane foams (IFD, CFD, tensile, tear, compression set).
ASTM D395
CompressionCompression set under constant force — fixture loading via UTM.
ASTM D412
TensileTension testing of vulcanized rubber and thermoplastic elastomers (dumbbell and ring specimens).
ASTM D413
Peel & adhesionAdhesion of rubber to fabric or flexible substrate (ply separation).
ASTM D429
Peel & adhesionAdhesion of rubber to rigid substrates (Methods A, B, C — tension and 90° peel).
ASTM D575
CompressionRubber properties in compression (deflection at load / load at deflection).
ASTM D624
TearTear strength of conventional vulcanized rubber and thermoplastic elastomers (Die A, B, C and trouser).
ASTM D6319 / D3578
TensileNitrile and rubber examination gloves — tensile strength and elongation requirements tested per ASTM D412.
ASTM D885
TensileTyre cords, tyre cord fabrics and industrial yarns made from manufactured fibres — tensile and adhesion methods.
EN 455-2
TensileMedical gloves — force at break requirements (single-use gloves).
IS 3400
TensileIndian Standard methods of test for vulcanized rubber — tensile stress-strain properties.
ISO 1798
TensileTensile strength and elongation at break of flexible cellular polymers.
ISO 1827
Peel & adhesionShear modulus and adhesion of rubber to rigid plates — quadruple-shear method (anti-vibration mounts).
ISO 2439
CompressionIndentation hardness (IFD/ILD) of flexible cellular materials — seating and mattress foams.
ISO 3386-1 / -2
CompressionStress-strain characteristics in compression of flexible cellular polymers (low- and high-density).
ISO 34-1 / -2
TearTear strength of rubber — trouser, angle (Die C) and crescent test pieces; small (Delft) test pieces.
ISO 36
Peel & adhesionAdhesion of rubber to textile fabrics.
ISO 37
TensileDetermination of tensile stress-strain properties of vulcanized and thermoplastic rubber. Equivalent to: IS 3400-1
ISO 4074
Puncture & burstNatural rubber latex condoms — tensile properties of test pieces.
ISO 7743
CompressionDetermination of compression stress-strain properties of rubber.
ISO 8067
TearTear strength of flexible cellular polymeric materials.
ISO 813
Peel & adhesionAdhesion of rubber to rigid substrate — 90° peel and tension methods.
ISO 814
Peel & adhesionAdhesion of rubber to rigid substrate — 90° peel and tension methods.
ASTM D5289
Cure & rheologyVulcanization characteristics with a rotorless cure meter — ML, MH, ts2 and t90 read from the cure curve. Equivalent to: ISO 6502, DIN 53529
ISO 6502
Cure & rheologyMeasurement of vulcanization characteristics with rotorless curemeters. Equivalent to: ASTM D5289, DIN 53529
DIN 53529
Cure & rheologyVulcanization characteristics and cure behaviour of rubber compounds. Equivalent to: ASTM D5289, ISO 6502
ISO 13145
Cure & rheologyViscosity and stress relaxation of unvulcanized rubber using a rotorless sealed shear rheometer.
ASTM D6204
Cure & rheologyProcessability of unvulcanized rubber with a rotorless shear rheometer — strain and frequency sweeps.
ASTM D6601
Cure & rheologyCure and after-cure dynamic properties with a rotorless shear rheometer.
Showing 1–8 of 32 standards